Interpenetrating dual cure resin compositions

ABSTRACT

Curable resin compositions are prepared containing a radiation-sensitive reactive diluent and a saturated polyol. Curing is accomplished by mixing the reactive diluent and the polyol with a polyisocyanate, followed by exposure of the resultant composition to radiation to polymerize the reactive diluent and then, by thermal curing, to form the hydroxyisocyanate (urethane) linkage. The fully cured resin composition is described as interpenetrated or one in which there is no cross-linking between the reactive diluent and urethane linked co-polymer. The interpenetrated resin compositions form tough and hard coatings on various substrates.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to resin compositions having utility as protective, transparent or translucent coatings for various substrate materials such as wood, paper, metal and plastics.

2. Description of the Art

The field of coating materials has undergone tremendous changes in recent years. One primary concern in the coating industry is the need to lower the emission of volatile hydrocarbons into the air. Under prior practices, coating compositions which are highly viscous were cut with a compatible solvent, such as benzene, toluene or xylene. These solvents aided in processing the coating composition during manufacture and in application to substrates.

In the curing of the coating, that is, the chemical bonding of the various components to form a polymer, the solvent is driven off by the thermal energy used to effect curing. As the thermal curing operation is ordinarily carried out by any number of end consumers, the resultant air quality in the consumer's plant and the atmosphere will depend on the steps which the consumer employs to trap the volatile emissions.

It should also be recognized that a considerable amount of thermal energy is expended in driving off volatile solvents. Aside from cost considerations, the necessary thermal energy to drive off the solvent may cause an undesirable side reaction in the coating or upon the substrate. This problem could be solved by gradually applying the thermal energy to the coated substrate, but with additional time required for the cure. Moreover, the cure rate is essentially independent of the energy required to drive off the solvent. Thus, the cured coating may entrain the solvent, giving rise to a poor coating, e.g. bubbles.

The problem facing the coating industry is, therefore, to provide a resin composition having the desirable properties of former resin composition, but not containing a volatile solvent which is emitted into the atmosphere during the thermal curing step.

Smith, et al., in U.S. Pat. No. 3,935,330 issued Jan. 27, 1976, suggested a coating composition containing, as required components, a reactive thermoset cross-linker and a reactive solvent which is both thermal and radiation sensitive. Exemplary of the thermoset cross-linkers disclosed in Smith et al are polyfunctional oxiranes, urea/formaldehyde resins and melamine/formaldehyde resins. The reactive solvents are generally described as materials containing both a vinyl polymerizable double bond and a functional group which is reactive under thermal activation.

The oligomers formed through the processing described in Smith et al are fully cross-linked or a penetrated resin composition. That is, the oligomers are a single, continuous complex randomly formed through the common thermosetting functional group. This patent also contemplates the addition of materials which will function to increase the molecular weight of the reactive solvent in the radiation curing step. These latter materials which are called radiation sensitive reactive components will copolymers through a vinyl radical with the reactive solvent. The resultant copolymer which still maintains its thermal curing functionality then forms a higher molecular weight oligomer with the reactive thermoset crosslinker.

The deficiency in the compositions disclosed by Smith et al lies in the properties of the penetrated oligomer. Specifically, the fact that the oligomer contains at least two thermosetting components and up to two different vinyl containing components leads to a considerable variance in the physical properties of oligomer. That is the variance in the molecular weight of the reactive solvent following the radiation cure must be considered in formulating the end product (oligomer). Similarily, the structure and molecular weight of the reactive solvent must be factored if the additional radiation sensitive component is present to predict the properties of the oligomer. Moreover, the final structure of the penetrated oligomer will vary considerably, if the reactive solvent has not been sufficiently cured by the radiation. That is, the reactive solvent is fully capable of undergoing thermal crosslinking even in the absence of any radiation curing. While this tends to lessen volatility when the radiation cure is incomplete the result is an unpredictably structured oligomer.

U.S. Pat. No. 3,028,367 issued Apr. 3, 1962 to O'Brion teaches the formation of thermosetting resins comprising a copolymer of a hydroxy alkyl acrylate and an alkyl acrylate together with a dihydric or trihydric alcohol and an organic diisocyanate. Organic thiol compounds are shown as useful in controlling the molecular weight of the copolymer portion of the resin. The copolymer which is hydroxy functional is preferably prepared using a free radical liberating agent in the presence dimethylformamide as a solvent. The solvent is removed following the preparation of the copolymer. The final resin composition is then prepared by reacting the copolymer with the alcohol and the isocyanate. Apparently the copolymer is of sufficiently low molecular weight that no solvent is required to lower the viscosity during application to a substrate.

Shur et al. in U.S. Pat. No. 3,772,062 issued November 13, 1973 discloses fiber-board coating compositions which are fully cured by actinic radiation. That is, the compositions are penetrating to the extent that all the components contain acrylic groups which are subject to free radical initiated bonding. The use of thermal energy for curing is stated to be avoided by the reference. The difficulty in attempting to use fully radiation cured resins is the lack of physical strength due to incomplete curing leaving a residue of acrylic monomer in the coating. U.S. Pat. No. 3,776,729 to Levy et al. issued Dec. 4, 1973 suggest washing off the non-polymerized monomer following the radiation cure. It is easily observed that fully radiation curable compositions are undesirable unless the cure is complete both from a cost and environmental view. Furthermore the inconsistence in the coating which results where not all the monomer has been cured or washed off can produce a product which will discolor or crack when exposed to later sources of radiation, i.e. sunlight.

It is therefore an object of this invention to prepare a curable coating which is essentially free from solvent emission.

It is a further object of this invention to prepare a curable coating wherein all the components are cured.

It is yet a further object of this invention to prepare a curable coating wherein the radiation sensitive reactive diluent and the thermally curable portion of the composition are interpenetrated.

These and other objects of the invention are fully discussed herein. Throughout the specification and claims temperatures are in centigrade degrees and percentages and ratios are by weight unless otherwise indicated.

SUMMARY OF THE INVENTION

An interpenetrating radiation-sensitive resin composition is prepared comprising:

(a) from about 40% to about 90% by weight of a saturated polyol; and,

(b) from about 10% to about 60% by weight of a reactive diluent having a radiation sensitive pi bond and having a boiling point greater than that of benzene;

and mixtures thereof.

A second embodiment of the present invention is an interpenetrating urethane-linking resin composition comprising:

(a) from about 40% to about 90% by weight of a saturated polyol; and

(b) from about 10% to about 60% by weight of a reactive diluent selected from the group consisting of the fully substituted polyacrylates and polymethacrylates of poly-functional alcohols, 2-ethylhexyl acrylate, isodecylacrylate, diallyl maleate N-vinyl-2-pyrrolidone, styrene, divinylbenzene and vinyl acetate, and mixtures thereof; and

(c) from about 80% to about 120% on a hydroxylisocyanate equivalent basis of a polyisocyanate.

Also within the scope of the present invention is the method for forming an interpenetrated urethane linked coating composition on a substrate involving the steps of radiation and thermal curing by:

(a) preparing a mixture containing:

(1) from about 40% to about 90% by weight of a saturated polyol; and

(2) from about 10% to about 60% by weight of a reactive diluent selected from the group consisting of the fully substituted polyacrylates and polymethacrylates of polyfunctional alcohols, N-vinyl-2-pyrrolidone, styrene, 2-ethylhexyl acrylate, isodecyl acrylate, diallyl maleate, divinylbenzene and vinyl acetate and mixtures thereof; and

(3) from about 80% to about 120% on a hydroxyl-isocyanate equivalent basis of a polyisocyanate;

(b) applying the mixture to a substrate and subjecting the coating so formed to a sufficient radiation to polymerize the reactive diluent thereby partially curing the coating; and,

(c) then exposing the partially cured coating of (b) to sufficient thermal energy to form the urethane link,

thereby forming the interpenetrated cured coating on the substrate.

DETAILED DESCRIPTION OF THE INVENTION

The present invention contemplates an interpenetrating resin composition which is both radiation and thermally cured. In the contemporary preparation and transportation of polyols for use in curable resins an inert ingredient such as toluene or xylene is included to facilitate processing. One aspect of the present invention deals with the displacement of these volatile inert solvents by distillation. Prior to the distillation process the reactive diluent containing at least one radiation sensitive pi bond is substituted as the carrier or solvent for the polyol.

The reactive diluent should not initially be present with the polyol if the polyol is to be formed through acrylic links in the prepolymer. That is where the polyol is for example a hydroxy-functional copolymer of methyl methacrylate, butyl acrylate, and hydroxyethyl acrylate formed through coupling of the acrylic groups the presence of the reactive diluent initially would result in a copolymer linked to the reactive diluent. In such cases the inert solvent is required until the saturated polyol has been formed and is substantially free of active acrylic (pi bond) groups. Particular examples of forming the saturated polyol from vinyl monomers in the presence of the inert solvent are discussed later in the specification.

Where the reactive diluent would not undergo polymerization through vinyl linkage with the monomers used to form the polyol all the components may be processed to the exclusion of the inert solvent. However, it is still desirable to process the polyol in the presence of the inert solvent as the latter material in any event is a superior to most of the reactive diluents. That is, inert solvents such as toluene provide lower viscosity and thus easier processing of the polyol.

Therefore in most aspects of the present invention a mixture of the saturated polyol and the reactive diluent will be separated from the inert solvent by distillation. The first parameter for the reactive diluent is therefore that it must have a boiling point above that of benzene which is a common inert solvent. More preferably the boiling point of the reactive diluent is greater than that of toluene another suitable inert solvent. For most embodiments the boiling point of the reactive diluent is between about 120° and 300° C where the upper temperature is reflective of the need to maintain a sufficiently low viscosity of the mixture of the saturated polyol and the reactive diluent. To effect complete removal of the inert solvent by distillation the inert solvent and the reactive diluent should not form an azeotropic mixture.

It is preferred that the reactive diluent be difunctional with respect to the radiation sensitive pi bond functional groups. The difunctionality ensures that cross-linking rather than linear polymerization is obtained during the radiation curing step. The same effect of difunctionality is obtained with a monofunctional reactive diluent if during the radiation cure a sufficient amount of a difunctional reactive diluent is present to ensure some cross-linking. Thus, if monofunctional reactive diluents are utilized a difunctional reactive diluent is preferably present in a weight ratio of from about 4:1 to about 1:4 to the monofunctional reactive diluent. Preferably this ratio is from about 3:1 to about 1:3.

A requirement for the reactive diluent is that it must not contain functional groups which are subject to thermal curing. This condition exists from the advantageous properties of the fully cured interpenetrated polymer. that is the reactive diluent does not contribute greatly to the strength of the cured composition even if the composition is interpenetrated, but where the reactive diluent could chemically bond into the polyol and polyisocyanate structure the overall strength of the cured composition is weakened.

It is also noted that thermally curable functionalities on the reactive diluent would cause the structure of the cured resin to be less predictable. That is the backbone of the polyol is formulated so that repeating units of the polyol is formulated so that repeating units of the various monomers will exist in a particular order. Often this order in the polyol is determined by the processing conditions such as the temperature, presence of catalysts, rate of addition of the monomers, and the duration of the reaction. All of the foregoing must be accomplished in a precise fashion to achieve the copolymer (polyol) which is then cured with the isocyanate.

Therefore any functional group on the reactive diluent which could combine at the conditions under which the polyol is formed or with the polyisocyanate in the final curing operation is to be avoided. Thus the reactive diluent must not contain hydroxyl, amine, carboxyl, primary and secondary amides, or isocyanate functional groups.

Where the polyol is formed by polymerization through a vinyl link (radiation sensitive pi bond) it is understood that the reactive diluent should not be present during polyol formation as the reactive diluent would then undergo a similar reaction leading to undesirable by-products. While the reactive diluent must not contain radicals which would cause the polyol/polyisocyanate resin to become a penetrated system substitutents which are non-reactive are permissible. That is the structure of the reactive diluent may contain any such non-reactive radical.

In addition to the foregoing requirements the reactive diluent preferably has a molecular weight of from about 80 to about 800, more preferably about 100 to about 400. Compounds meeting the molecular weight requirement are suitable to lower the viscosity of the polyol.

Examples of monofunctional reactive diluents include the esters of acrylic and methacrylic acid such as methyl acrylate, methyl methacrylate; ethyl acrylate and methacrylate; propyl and isopropyl acrylate and methacrylate; butyl, isobutyl, and tertiary butyl acrylates and methacrylates; n-pentyl and the isopentyl acrylates and methacrylates; n-hexyl and the isohexylacrylates and methacrylates.

Other monofunctional vinyl reactive diluents include the n-heptyl and iso-heptyl acrylates and methacrylates; and octyl and the iso-octyl acrylates and methacrylates. Of this latter category an especially preferred reactive diluent is 2-ethylhexyl acrylate.

Further examples of suitable reactive diluents are the acrylates and methacryltes of the normal and isomeric forms of nonyl, decyl, undecyl, dodecyl, tridecyl and tetradecyl alcohols. Moreover the foregoing esters of acrylic and methacrylic acid may contain non-radiation sensitive unsaturation in the alcohol radical as well.

Additional monofunctional radiation active pi bond compounds which may be used as a reactive diluent include diallyl maleate, diallyl fumarate, vinyl acetate and N-vinyl-2-pyrrolidone, especially the latter compound. The maleate and fumarate compounds actually contain three carbon-carbon pi bonds however only the interior double bond in the maleic (or fumaric) acid backbond is reactive to ultraviolet radiation. Examples of an aromatic monofunctional radiation sensitive pi bond reactive diluents are vinyl toluene and styrene.

The highly preferred reactive diluents of the present invention are those having more than one radiation sensitive pi bond. Such compounds are ordinarily the esters of acrylic or methacrylic acid and a polyhydric alcohol. It will be remembered that when utilizing such reactive diluents that the hydroxyl functionality of the polyhydric alcohol should be fully substituted with the acrylic or methacrylic acid to avoid complete cross-linking (a penetrated polymer) upon addition of the polyisocyanate.

Examples of the foregoing difunctional diluents are ethylene glycol diacrylate and dimethylacrylate; isopropylene and propylene glycol diacrylate and dimethacrylate. Similarily the diol diacrylates and dimethacrylates of butane, pentane, hexane, heptane and so forth through the thirty-six carbon diol are useful in the present invention as reactive diluents. Of particular interest are 1,6-hexane diol diacrylate, diethylene glycol diacrylate, trimethylol propane triacrylate, and pentaerythritol tetraacrylate.

The second component of the present invention is the saturated polyol. The polyol is required in the present invention to form the urethane linkage with the isocyanate through the hydroxyl functionality of the polyol. The urethane linkage is represented as ##STR1## It is further required that the saturated polyol must as its name implies contain at least two hydroxy functional groups to ensure the proper degree of cross-linking during the thermal cure step.

The saturated polyol may be an alkyl or cycloalkyl polyol, an ester linked polyol, an ether linked polyol, an ether and ester linked polyol or hydroxy functional acrylic copolymers. In fact a general definition of the polyols is obtained above from the polyhydric alcohols which were condensed with the acrylic and methacrylic acid to form the reactive diluents. That is the precursor polyhydric alcohol definition for use in making the reactive diluents is identical to that of the saturated polyol.

Specific examples of alkyl and cycloalkyl polyols include 2,5-hexanediol available from Aldrich Chemical, 1,6-hexanediol, available from Celanese Chemical, ethylene glycol available from Baker, Dimerol a 36 carbon essentially linear diol available from General Mills Chemicals, Inc., glycerol, 1,2,6-hexanetriol available from Union Carbide, pentaerythritol, and 1,4-cyclohexane diol. Additional examples of such polyols include Polybd R-45HT a Butadiene diol having an approximate molecular weight of 2800 available from Arco and Trimethylol propane available from Celanese.

The ester linked saturated diols of the present invention are more particularly described as polyols where the predominate linkage (functional group other than the hydroxyl) are ester radicals. The ester linked saturated polyols are structurally represented as ##STR2## where R and R' are organic residues which contain at least two hydroxyl radicals and at least one ester link.

Examples of ester linked saturated polyols include Niax PCP0200 and PCP0240 both available from Union Carbide and having respective molecular weights of approximately 530 and 2000. Both of the foregoing compounds are diols. Niax PCP0300 also available from Union Carbide is a Caprolactone-ester triol having approximately molecular weight of 540. Niax PCP0310 also available from Union Carbide is a Caprolactone-ester triol having a molecular weight of approximately 900.

The ether linked saturated polyols of the present invention include compounds such as diethylene glycol and triethylene glycol both available from Fisher. Further ether linked saturated polyols useful in the present invention include the Polymeg Q0650, Q0650, Q0100, and Q0200 all of which are ether diols available from Quaker having a respective molecular weight of approximately 650, 1000 and 2000. Pluarcol P1010 having an approximately molecular weight of 1050 available from Wyandotte is an example of a polypropylene oxide ether linked diol useful in the present invention. Similar Wyandotte products useful as saturated polyols in the present invention include Pluracol TP440 and 150 which are propylene oxide ether linked triols having respective molecular weights of approximately 425 and 1560. In similar fashion Pluaracol GP3030 is another saturated polyol suitable for the present invention available from Wyandotte. The foregoing material is a glycerine polypropylene ether linked triol having an approximate molecular weight of 2900.

Additional Pluracols useful in the present invention include Pluarcol PEP450 wich is a pentaerythritol polypropylene oxide ether linked tetrol having a molecular weight of 405 and Pluracol 493 an ether linked tetrol having a molecular weight of approximately 3630.

Ester and ether linked saturated polyols suitable in the present invention are described structurally as ##STR3## where R, R' and R" are organic residues containing at least two hydroxyl radicals and at least one ester and one ether linkage.

The remaining compositional aspect of the present invention requires the presence of an organic polyisocyanate compound. That is to assure a proper degree of cross linking with the saturated polyol the isocyanate must by definition contain at least two isocyanate functional groups. Preferably the polyisocyanate will contain from two to five, most preferably two or three isocyanate functional groups in the molecule.

Suitable polyisocyanates include ethylene diisocyanate, trimethylene diisocyanate, hexamethylene diisocyanate, propylene-1,2-diisocyanate, ethylidene diisocyanate, cyclopentylene-1,3-diisocyanate, the 1,2-, 1,3- and 1,4-cyclohexylene diisocyanates, the 1,3-, and 1,4-phenylene diisocyanates, polymethylene polyphenylene-isocyanates, the 2,4-, and 2,6-toluene diisocyanates, the 1,3-, and 1,4-xylylene diisocyanates, bis(4-isocyanatophenyl)methane, 4,4'-diphenyl-propane diisocyanates, bis(2-isocyanatoethyl) carbonate, 1,8-diisocyanato-p-methane, 1-methyl-2,4-diisocyanato-cyclohexane, the chlorophenylene diisocyanates, naphthalene-1,5-diisocyanate triphenylmethane-4,4',4"-triisocyanate, isopropylbenzene-alpha-4-diisocyanate, 5,6-bicyclo[2.2.2] hept-2-ene diisocyanate, 5,6-diisocyanatobutylbicyclo [2.2.11]hept-2-ene and similar polyisocyanates.

Of particular interest in the present invention are trimethylene hexamethyl diisocyanate available from VEBA, heptadecyl (C17) diisocyanate, DDI 1410 an aliphatic C-36 diisocyanate available from General Mills Chemicals, Inc. (generally diisocyanates having from 12 to 40 carbons in the aliphatic radical may be used in the present invention), toluene diisocyanate available from Allied Chemical, isophorone diisocyanate available from VEBA and Desmodur N an aliphatic triisocyanate from Mobay. Desmodur N is more particularly defined the tri-isocyanate adduct of 3 moles of hexamethylene dissocyanate and water having an isocyanate equivalent weight as later defined of 191 grams. Other adducts or prepolymers of the polyisocyanate include Desmodur L and Mondur CB which are the adducts of toluene diisocyanate. The foregoing materials have an isocyanate equivalent weight of approximately 250 grams.

In both the compositional and method aspects of the present invention the saturated polyol is present at a level of from about 40% to about 90% preferably from about 50% to about 80% by weight. The reactive diluent is present at from about 10% to about 60%, preferably from about 20% to about 80% by weight.

The amount of the polyisocyanate utilized in forming the interpenetrating compositions of the present invention is expressed as a percentage equivalent weight basis with respect to the hydroxyl functionalities of the saturated polyol. Desirably each hydroxyl functional group on the saturated polyol will react on a 1:1 stoichometric basis with the isocyanate functionality on the polyisocyanate compound. It is quite feasible however to form the urethane linkage using from about 80% to 120% preferably from about 95% to a105% on a hydroxyl-isocyanate equivalent basis of the polyisocyanate.

To determine the amount of the polyisocyanate required for a given saturated polyol the hydroxyl or isocyanate equivalent weight of the respective polyol or polyisocyanate is determined as that weight in grams of the material which contains 1 gram equivalent weight of the respective functional group. More particularly to determine the number of equivalents in a given saturated polyol the hydroxyl value is first determined by known methods and reported in milligrams of potassium hydroxide. The calculation to determine the hydroxyl equivalents is then given by the following equation: ##EQU1## where 56,100 is the milligram equivalent weight of potassium hydroxide.

Alternatively if the weight percentage of the hydroxyl groups in the saturated polyol is known the hydroxyl equivalent is determined as follows: ##EQU2## where 17 is the equivalent weight of the hydroxyl radical and the weight percent OH is the percentage of the saturated polyol which is hydroxyl groups.

In similar fashion the isocyanate equivalent may be determined if the weight percent of the isocyanate functional groups in the polyisocyanate is known. This equation is given below where 42 is the molecular weight of an isocyanate functional group and the weight percent NCO is that portion of polyisocyanate made up of isocyanate functional groups. ##EQU3##

A highly desirable variable of the present invention is to formulate the saturated polyol and the polyisocyanate such that the sum of the isocyanate functionability and the hydroxyl functionality is greater than four. That is if the polyisocyanate is a diisocyanate then the saturated polyol should be a triol. Similarly where triisocyanates are utilized it is desirable that the saturated polyol be a diol or triol. The value of this discovery resides in the fact that in forming the interpenetrated urethane linked resin composition that a higher degree of cross-linking of the polyol annd the polyisocyanate will occur under the foregoing conditions as opposed to the situation where the polyisocyanate and the saturated polyol contain the same number of functional groups. The foregoing discussion is not to be confused with the determination of the hydroxylisocyanate equivalents discussed immediately above.

In the present invention the saturated polyol and the reactive diluent are ordinarily premixed prior to the addition of the polyisocyanate component. There are two basic reasons for following this order of addition. The first reason is that the reactive diluent functions to lower the viscosity of the saturated polyol and thus permits further mixing with the polyisocyanate. In the absence of premixing the saturated polyol would often be too viscous to process. Even if the saturated polyol is of sufficiently low viscosity to permit addition of the polyisocyanate before the reactive diluent this order of addition is not preferred due to the fact the saturated polyol and the polyisocyanate can react to form the urethane linkage at room temperature. When this is the case the saturated polyol and the polyisocyanate may not be stored together for long periods of time such as in a warehouse. It is believed that when the preferred order of addition (reactive diluent and saturated polyol then polyisocyanate) is followed that the reactive diluent functions not only to lower the viscosity of the saturated polyol but also slow the urethane formation at room temperature to allow time for application to the substrate.

The second reason for mixing the saturated polyol and the reactive diluent prior to the addition of the polyisocyanate is related to the preparation of the saturated polyol in the first instance. For example when the saturated polyol is the reaction product of acrylic acid, butyl acrylate and hydroxyethl acrylate it is necessary to include some solvent to lower the viscosity of the polyol. Toluene or xylene are preferred inert solvents for the preparation of the aforedescribed polyol. To avoid atmospheric pollution the reactive diluent is added to the mixture of the saturated polyol and the inert solvent followed by distilling off the inert solvent. The inert solvent is then recovered for reuse while the low viscosity mixture of the saturated polyol and the reactive diluent are drawn off for use in the resin composition. A preferred reactive diluent which may be added to the saturated polyol prior to distillation of the aromatic solvent is 1,6-hexanediol diacrylate.

UTILIZATION

The compositions of the present invention comprising the saturated polyol, the reactive diluent, and the polyisocyanate are applied to substrates such as wood, metal, paper, or plastics by any convenient method such as knife blade, brush, or spray. The coated surface is then exposed to sufficient radiation which may be either particulate or non-particulate radiation to cure the reactive diluent through the radiation sensitive pi bonds. Suitable sources of particulate and non-particulate ionizing radiation include ultraviolet light or radioactive sources such as are described in U.S. Pat. No. 3,935,330 issued Jan. 27, 1976 to Smith et al. To enhance the rate of radiation curing of the reactive diluent free radical initiators may be included in the composition such as benzoin, benzoin ethers, Michler's Ketone and chlorinated polyaromatic hydrocarbons. Other free radical initiators are ordinarily organic peroxides, hydroperoxides, per acids, per esters, azo compounds, ditertiary butyl peroxide, benzoyl peroxide, 2,4-dichlorobenzoyl peroxide, tertiary butyl hyproperoxide, 2,5-dimethyl -2,5-bis (hydroperoxy)-hexane, peracetic acid perbenzoic acid, tertiary butyl peroxypivalate, tertiary butyl peracetic acid and azo-bis-isobutyl nitrile. The free radical initiator may be present at from about 0.01 to about 20% by weight of the radiation curable components.

To ensure that the reactive diluent does not polymerize prior to the addition of the polyisocyanate a free radical inhibitor may be added to the mixture of the saturated polyol and the reactive diluent. Examples of suitable inhibitors include hydroquinone and the methyl ether thereof or butylated hydroxy toluene at a level of from about 5 ppm to about 2000 ppm by weight of the radiation curable components.

The amount of radiation necessary to cure the reactive diluent will of course depend on the angle of exposure to the radiation, the thickness of the coating to be applied, and the amount of reactive diluent in the coating composition as well as the presence or absence of a free radical initiating catalyst. For any given composition experimentation to determine the amount of radiation sensitive pi bonds are cured following exposure to the radiation source is the best method of determining the amount and duration of the radiation required.

The thermal curing operation is best carried out between the temperatures of about 0° to about 300° C preferably from about 20° C to about 200° C. To operate with a minimal amount of thermal energy expended to form the urethane linkage a catalyst may be used to promote the reaction. Examples of such urethane catalysts include triethylene diamine, morpholine, N-ethyl-morpholine, dimethyl piperaxine, triethylamine, N,N,N',N'-tetramethylbutane-1,3-diamine, dibutyltin dilaurate, stannous octoate, stannous laurate, dioctyltin diacetate, lead octoate, stannous oleate, stannous tallate, dibutyltin oxide, and hexabutylditin as well as other art recognized urethane catalysts. Typical levels of the urethane catalyst are from about 0.001% to about 5% by weight of the urethane linking components.

The amount of time required to effect the thermal cure in the present invention depends as in the case of the radiation cure upon the amount of the thermal cure ingredients, the thickness of the coating, and other factors intrinsic to the system. If the saturated polyol and the polyisocyanate are included in the interpenetrating compositions on a hydroxyl-isocyanate equivalent basis the rate and completeness of thermal cure may be determined by analyzing for free isocyanate or free hydroxyl presence in the coating. Where more or less than the equivalent amount of the polyol or the polisocyanate is included in the composition the degree of thermal curing is most conveniently measured by determining the presence of the functional group present in excess of the equivalent weight versus the theoretical amount of that component which should be present following the thermal cure. In cases where the thermal cure is not completely affected additional thermal energy may be applied to complete the urethane formation.

It is recommended that experimentation be utilized to determine the proper duration required for the thermal cure. Generally the amount of time required to affect the thermal cure under normal operating conditions will be from about 1 to about 30 preferably from about 5 to about 10 minutes.

Additional components which may be included in the present invention include pigments, dyes, reflective materials and so forth. Minor amount of compounds which have both radiation sensitive pi bonds and thermally curable functional groups may be present in the resin composition. Such materials include hydroxyethyl acrylate and pentaerythritol triacrylate. Both of the foregoing components contain both acrylate and hydroxy functional groups. As long as such components are present at not more than about 10% by weight the degree of the penetration of the interpenetrated coating compositions will not be substantially affected and the inclusion of these materials may be tolerated.

The following are examples of the present invention.

EXAMPLE I

An interpenetrating radiation sensitive resin composition is prepared as follows: The following components are used to form a hydroxy functional acrylic copolymer:

    ______________________________________                                                             Parts by Weight                                            ______________________________________                                         xylene                40                                                       methyl methacrylate   25                                                       n-butylacrylate       25                                                       hydroxy-ethyl acrylate                                                                               8.82                                                     ditertiary butyl peroxide                                                                            1.18                                                                           100.00                                                   ______________________________________                                    

The acrylic functional compounds are placed in a premix tank and thoroughly stirred for 10 minutes. The ditertiary butyl peroxide is added to the premix tank and then stirred for 20 minutes.

A kettle is then set for reflux conditions and the xylene is charged into the kettle with a nitrogen sparge. One tenth of the premixed acrylic monomers and the ditertiary butyl peroxide are then added into the kettle. The limited addition of premix is useful in controlling the highly exothermic acrylic polymerization.

The mixture in the kettle is then stirred and refluxed at about 135° C for about 15 minutes. The remainder of the premix is fed in to the kettle over a period of 90 minutes with constant reflux throughout the addition. After an additional one hour period a sample of the mixture in the kettle is withdrawn to determine the solids content which for the present exammple should be about 60% by weight.

The reaction mass is then cooled to temperature below about 50° C. The hydroxy functional acrylic copolymer mixture has a Gardner color of about 2, a viscosity of 30-50 poise, is clear and has a hydroxyl value of 70-75 mg KOH per gram and a hydroxyl equivalent weight of 1274.

18.520 kilograms of the reaction mass are then mixed with 2.118 kilograms of Pluracol PEP650 which has an equivalent weight of 145.7. To this mixture 5.96 grams of hydroquinone are added to inactivate any trace of the ditertiary butyl peroxide catalyst. It is preferable to add hydroquinone in a heated portion of xylene to ensure that the former material is dissolved or dispersed. 4.77 kilograms of 1,6-hexane diol diacrylate (the reactive diluent) are then added to the kettle. Heat and vacuum are then simultaneously applied to distill off the xylene. The kettle temperature at this point is between about 55 and 65° C with the vacuum at about 20 mm Hg.

The kettle is then maintained at about 60° C under the highest possible vacuum until xylene distillation ceases usually in about one hour at 200 microns of absolute pressure.

When the distillation is completed the vacuum is opened to air and a sample is removed and tested for solids analysis, The resultant product is a clear, water white liquid having a viscosity of about 200 poise at 50° C. The solids content following distillation of the xylene is greater than 95% and the saturted polyol in the composition has a hydroxyl value of 110. The Gardner color value is 1- and a gas liquid chromotography test indicates that only about 1.5% of the xylene remains in the mixture following distillation.

The foregoing interpenetrating radiation sensitive resin composition is mixed with any of the polysisocyanate compounds in accordance with the present invention to form the urethane linking radiation sensitive resin composition. Similar compositions are obtained where the methyl methacrylate the butyl acrylate and the hydroxyethyl acrylate are combined in a molar ratio of from about 4:1:1 to about 1:4:3.

EXAMPLE II

An interpenetrating radiation sensitive resin composition is prepared in the following manner:

The premix tank is charged with methylmethacrylate, styrene, n-butyl acrylate, and hydroxy-ethyl methacrylate and stirred for a period of about 10 minutes. Tertiary butyl perbenzoate is added as a free radical catalyst and stirring is continued for about 20 minutes.

The kettle is set for total reflux and charged with xylene as the inert solvent. Approximately 10 percent of the premix comprising the monomers and the free radical catalyst are added to the kettle. The nitrogen sparge the premix then set in the kettle.

The stirrer in the kettle is then activated and the kettle heated to reflux at from about 130°-135° C under reflux conditions for a period of about 20 minutes. The remainder of thepremix is fed in at a uniform rate over a period of about 4 hours maintaining reflux throughout the addition period. At about one hour after completion of the premix addition the solids and free monomer content of the composition in the kettle is determined to ensure substantial completion of the hydroxy functional acrylic copolymer. The composition in the kettle comprises:

    ______________________________________                                         Contents              Parts by Weight                                          ______________________________________                                         xylene                40.00                                                    methyl methacrylate   19.16                                                    styrene               19.16                                                    n-butyl acrylate       6.77                                                    hydroxy-ethyl methacrylate                                                                           12.64                                                    tertiary butyl perbenzoate                                                                           2.27                                                                           100.00                                                   ______________________________________                                    

The mixture of the inert solvent, the free radical catalyst and the hydroxy functional acrylic copolymer containing methyl methacrylate, styrene, n-butyl acrylate, and hydroxyethyl methacrylate units form a clear mixture having a Gardner color of 3, a viscosity of 35-45 poise and a hydroxyl value of 90-95 mg KOH per gram.

The mixture is cooled to below 50° C and the xylene is removed as in Example I and replaced with 13.61 prts of 1,6-hexane diol diacrylate as the reactive diluent.

The foregoing composition is then used to form an interpenetrating urethane-linking radiation sensitive resin composition as follows:

    ______________________________________                                         Content           Parts by Weight                                                                              m.e.q.                                         ______________________________________                                         Hydroxy functional                                                                               58.9          95.2                                            acrylate copolymer                                                            Desmodur-N 100    18.2          95.2                                           V-pyrol (N-vinyl                                                                2-pyrrolidone)   20.8                                                         Vicure 10 (benzoin ether                                                        photoinitiator)  1.8                                                          Hexabutyl ditin   0.3                                                                            100.0                                                        ______________________________________                                    

The V-pyrol is an additional amount of reactive diluent added to the interpenetrating radiation sensitive composition to further lower the viscosity. The addition of the V-pyrol forms a stronger copolymer with the 1,6-hexane diol diacrylate following the radiation cure than does a homopolymer of the 1,6-hexane diol diacrylate and may be so varied between a ratio of 4:1 to about 1:4. The Vicure 10 is an ultraviolet initiator included at a level of 5 parts per 100 based on the total amount of reactive diluent in the composition. The hexabutyl ditin functions as a urethane catalyst and is included at a weight of 0.5 parts per 100 based on the weight of the urethane copolymer.

The foregoing interpenetrating urethane-linking radiation sensitive resin composition is then applied to a substrate and exposed to ultraviolet radiation to effect the radiation cure followed by thermal curing to give a strong high gloss interpenetrated urethane linked coating composition.

EXAMPLE III

An interpenetrated urethane-linking radiation sensitive resin composition is prepared as follows:

    ______________________________________                                         Component            Parts by Weight                                           ______________________________________                                         Hydroxy functional acrylic                                                     copolymer from Example I                                                                            72.8                                                      1,6-hexane diol diacrylate                                                                          15.6                                                      Desmodur-N 100       18.2                                                      V-pyrol              20.8                                                      Vicure 10             1.8                                                      Hexabutyl ditin       0.3                                                      ______________________________________                                    

The foregoing composition when treated with ionizing radiation to effect the radiation cure step and then by thermal cure to form the urethane linkage provides a strong tough coating on a substrate.

EXAMPLE IV

The following components were combined to prepare an interpenetrating urethane-linking radiation sensitive resin composition.

    ______________________________________                                         Components   Source       Equivalents                                                                              Weight                                     ______________________________________                                         Ethylene glycol                                                                             Baker Reagent                                                                  Grade        134 eq     4.13 kg                                   Desmodur-N (Des-N)                                                                          Mobay Chem. Co.                                                                             134 eq    25.47 kg                                   1,6-hexanediol                                                                              Celanese Chem.                                                    diacrylate (HDODA)                                                                          Co                     12.8 kg                                    Vicure 10    Stauffer Chem.          0.64 kg                                   photoinitiator                                                                              Co.                                                               Hexabutyl ditin                                                                             Ventron Chem.                                                     (HBDT)       Co.                     0.09 kg                                   ______________________________________                                    

The coating materials of Example IV have a reactive diluent to urethane linking component weight ratio of 3:7 while the saturated polyol and the polyisocyanate are stoichiometrically balanced. The Vicure 10 photoinitiator is present at 5 parts per 100 based on the reactive diluent (HDODA). The hexabutyl ditin is present as a urethane linking catalyst at a level of 0.3 parts per hundred based upon the combined weight of the polyisocyanate and the saturated polyol.

The coating composition formed from the present example was applied to glass, black plate, and bonderite treated steel panels with 1.5 mm doctor blade. Each of the sample panels was cured by ultraviolet exposure by feeding the plates for 5 passes each at a rate of 60 feet per minute on a moving belt past an ultraviolet light source which is a 24- 200 watt/linear inch mercury vapor lamp in air. The thermal cure to form the urethane linkage was effected in a forced air oven over a period of 5 minutes at 150° C.

The properties of the coating prepared in accordance with this example are shown in Table 1.

EXAMPLES V- XXVI

Examples V-XXVI are prepared in accordance with Example IV in the example with the exception of replacing the ethylene glycol on an equivalent basis with the saturated polyols listed below.

    __________________________________________________________________________     Example No.                                                                           Saturated Polyol                                                                          Polyol Source                                                                           Polyol Description                                  __________________________________________________________________________     V      2,5-hexanediol                                                                            (Aldrich)                                                                               C.sub.6 diol                                        VI     Dimerol    (General Mills                                                                 Chemicals, Inc.)                                                                        C.sub.36 diol                                       VII    diethylene glycol                                                                         (Fisher) Ether diol, MW-106                                  VIII   Triethylene glycol                                                                        (Fisher) Ether diol, MW-150                                  IX     Niax PCP0200                                                                              (Union Carbide)                                                                         Ester diol, MW-530                                  X      Niax PCP0240                                                                              (Union Carbide)                                                                         Ester diol, MW-2000                                 XI     Polymeg Q0650                                                                             (Quaker) Ether diol, MW-650                                  XII    Polymeg Q01000                                                                            (Quaker) Ether diol, MW-1000                                 XIII   Polymeg Q02000                                                                            (Quaker) Ether diol, MW-2000                                 XIV    Polybd R-45HT                                                                             (Arco)   Butadiene diol, MW-2800                             XV     Pluracol P1010                                                                            (Wyandotte)                                                                             PO ether diol, MW-1050                              XVI    Trimethylol propane                                                                       (Celanese)                                                   XVII   Pluracol TP440                                                                            (Wyandotte)                                                                             TMP-PO ether triol, MW-425                          XVIII  Pluracol TP1540                                                                           (Wyandotte)                                                                             TMP-PO ether triol, NW-1650                         XIX    Glycerol   (Baker)                                                      XX     Pluracol GP3030                                                                           (Wyandotte)                                                                             Glycerine-PO ether triol, -   MW-2900               XXI    Niax PCP0300                                                                              (Union Carbide)                                                                         Caprolactone-ester triol,                                                      MW-540                                              XXII   Niax PCP0310                                                                              (Union Carbide)                                                                         Caprolactone-ester triol,                                                      MW-900                                              XXIII  1,2,6-hexanetriol                                                                         (Union Carbide)                                              XXIV   Pluracol PEP450                                                                           (Wyandotte)                                                                             Pentaerythritol-PO ether                                                       tetrol, MW-405                                      XXV    Pluracol 493                                                                              (Wyandotte)                                                                             Ether tetrol, MW-3630                               XXVI   Methyl methacrylate,                                                                      (General Mills                                                      n-butyl acrylate, and                                                                     Chemicals, Inc.)                                                                        Hydroxy functional acrylic                                 hydroxyethylacrylate                                                                               copolymer prepared according                               copolymer           to Example I                                        __________________________________________________________________________

The properties of the urethane linked coatings prepared in accordance with Examples V-XXVI shown in Table I below.

                                      TABLE I                                      __________________________________________________________________________     VARIOUS SATURATED POLYOLS                                                                     IV     V           VII   VIII  IX                                              Ethylene                                                                              2,5 Hexane                                                                           VI    Diethylene                                                                           Triethylene                                                                          Niax                             Example Number Polyol Name                                                                    glycol diol  Dimerol                                                                              glycol                                                                               glycol                                                                               PCP0200                          __________________________________________________________________________     OH eq. wt.     30.9   59.0  2500  53.06 75.09 262.0                            Weight in grams                                                                               12.4   17.7  25.0  5.31  7.51  26.2                             1,6-hexanediol diacrylate (gms)                                                               38.4   32.2  18.9  10.46 11.40 19.4                             Desmodur N-100                                                                 Weight in grams                                                                               76.4   57.3  19.1  19.1  19.1  19.1                             Vicure 10 at 5 phr                                                                            1.92   1.61  0.95  0.52  0.57  0.97                             Hexabutyl ditin at 0.3%                                                                       0.27   0.23  0.13  0.07  0.08  0.14                             Solution Appearance                                                                           Hazy               Hazy  Hazy  Clear                            Film Appearance                                                                               Smooth Smooth                                                                               Smooth                                                                               Cratered                                                                             Semi-hard                                                                            Smooth                           Adhesion % Loss Tape Test:                                                     Black Plate    100    100   100   100   100   100                              Bonderite 100   0      0     0     0     0     0                               G.E. Extensibility                                                             Black Plate     40-60  60    60   40-60 20-40 40-60                            Gardner - Reverse Impact                                                       Bonderite 100  120-130                                                                               160   160   100-120                                                                              160   150-160                          Pencil Hardness                                                                Scatch         3H     H     3H    6H    6H    HB                               Cut through    5H     4H    5H    9H    6H    H                                Sward Rocker Hardness                                                          % of glass     24%    34%   10%   20%   12%   6%                               MIBK resistance                                                                               NA     NA    NA    NA    NA    NA                               24 hour chemical resistance                                                    H.sub.2 O      Soft   V.S.S.                                                                               Soft  S.Soft                                                                               S.Soft                                                                               Soft                             20% NaOH       NA     NA    NA    NA    NA    V.Soft                           40% H.sub.2 SO.sub.4                                                                          NA     NA    NA    Soft  Swollen                                                                              Soft                                            X      XI    XII   XIII  XIV   XV                                              Niax   Polymeg                                                                              Polymeg                                                                              Polymeg                                                                              Polybd                                                                               Pluracol                         Example Number Polyol Name                                                                    PCP0240                                                                               Q0650 Q01000                                                                               Q02000                                                                               R-45HT                                                                               P1010                            __________________________________________________________________________     OH eq. wt.     1000.0 330.0 500.0 1001.18                                                                              1204.0                                                                               519.5                            Weight in grams                                                                               25.0   33.0  30.0  30.0  24.08 51.95                            1,6-hexanediol diacrylate (gms)                                                               12.8   22.3  17.8  15.3  11.96 30.45                            Desmodur N-100                                                                 Weight in grams                                                                               4.8    19.1  11.5  5.7   3.82  19.1                             Vicure 10 at 5 phr                                                                            0.64   1.12  0.89  0.77  0.60  1.52                             Hexabutyl ditin at 0.3%                                                                       0.09   0.16  0.12  0.11  0.08  0.21                             Solution Appearance                                                                           Hazy   V.S.Haze                                                                             Clear Hazy  Clear                                  Film Appearance                                                                               Smooth Smooth                                                                               Smooth                                                                               Smooth                                                                               Hazy  Hazy                             Adhesion % Loss Tape Test:                                                     Black Plate    80     0     0     5     15     0                               Bonderite 100   0     0     0     0      0     0                               G.E. Extensibility                                                             Black Plate    60     40-60 60    40-60 40-60 60                               Gardner - Reverse Impact                                                       Bonderite 100  160    160   160   160   160   160                              Pencil Hardness                                                                Scratch        5B     B     6B    6B    4B    4B                               Cut through    3B     HB    3B    5B    3H    5B                               Sward Rocker Hardness                                                          % of glass     14%    4%    6%    4%    4%    2%                               MIBK resistance                                                                               NA     NA    NA    NA    NA    NA                               24 hour chemical resistance                                                    H.sub.2 O      Soft   V.Soft                                                                               V.Soft                                                                               S.Soft                                                                               Soft  Soft                             20% NaOH       S.Soft Soft  S.Soft                                                                               Soft  Slight                                                                               Slight                           40% H.sub.2 SO.sub.4                                                                          S.Soft Dissolved                                                                            Dissolved                                                                            Soft  Slight                                                                               Swollen                                         XVI    XVII  XVIII       XX    XXI                                             Trimethylol                                                                           Pluracol                                                                             Pluracol                                                                             XIX   Pluracol                                                                             Niax                             Example Number Polyol Name                                                                    Propane                                                                               TP440 TP1540                                                                               Glycerol                                                                             GP3030                                                                               PCP0200                          __________________________________________________________________________     OH eq. wt.     44.67  142.0 525.0 30.67 972.0 176.4                            Weight in grams                                                                               4.47   14.2  26.25 3.07  24.3  17.64                            1,6-hexanediol diacrylate (gms)                                                               9.92   14.3  15.36 9.50  12.45 15.75                            Desmodur N-100                                                                 Weight in grams                                                                               19.1   19.1  9.60  19.1  4.78  19.1                             Vicure 10 at 5 phr                                                                            0.5    0.71  0.77  0.48  0.63  0.79                             Hexabutyl ditin at 0.3%                                                                       0.07   0.10  0.11  0.07  0.09  0.11                             Solution Appearance         Hazy  S.Haze                                                                               Clear                                  Film Appearance                                                                               Sl.rough                                                                              Smooth                                                                               V.Small                                                                              Smooth                                                                               Smooth                                                                               Rough                            Adhesion % Loss Tape Test:  bubbles                                            Black Plate    100    85    95    100   0     60                               Bonderite 100   0      0     0     0    0      0                               G.E. Extensibility                                                             Black Plate    60     60    60    20-40 40-60 60                               Gardner - Reverse Impact                                                       Bonderite 100  80-100 160   160   140-150                                                                              160   150-160                          Pencil Hardness                                                                Scratch        4H     7H    6B    2H    6B    3H                               Cut through    6H     8H    6B    8H    6B    6H                               Sward Rocker Hardness                                                          % of glass     22%    16%   4%    22%   2%    14%                              MIBK resistance                                                                               NA     NA    NA    NA    NA    NA                               24 hour chemical resistance                                                    H.sub.2 O      NA     NA    Soft  NA    Soft  Soft                             20% NaOH       NA     NA    S.Soft                                                                               NA    Soft  NA                               40% H.sub.2 SO.sub.4                                                                          NA     NA    Dissolved                                                                            NA    Swollen                                                                              NA                                              XXII   XXIII XXIV  XXV   XXVI                                                  Niax   1,2,6 Pluracol                                                                             Pluracol                                                                             Same As                                Example Number Polyol Name                                                                    PCP0310                                                                               Hexanetriol                                                                          PEP450                                                                               493   Example I                              __________________________________________________________________________     OH eq. wt.     301.3  45.0  100.7 913.8 760.0                                  Weight in grams                                                                               30.13  11.3  25.3  22.85 51.1                                   1,6-hexanediol diacrylate (gms)                                                               21.10  25.3  31.0  11.85 34.1                                   Desmodur N-100                                                                 Weight in grams                                                                               19.1   47.8  47.75 4.78  12.8                                   Vicure 10 at 5 phr                                                                            1.05   1.27  1.55  1.60  1.7                                    Hexabutyl ditin at 0.3%                                                                       0.15   0.18  0.22  0.08  0.3                                    Solution Appearance          Clear                                                                               S.Haze                                                                               Clear                                  Film Appearance                                                                               Smooth Smooth                                                                               Smooth                                                                               Smooth                                                                               Smooth                                 Adhesion % Loss Tape Test:                                                     Black Plate    100    96    100   100   100                                    Bonderite 100  100     0     0     0     0                                     G.E. Extensibility                                                             Black Plate    40-50  60    40-60 20-40 5-10                                   Gardner - Reverse Impact                                                       Bonderite 100  150-160                                                                               120-130                                                                              160   160   15-18                                  Pencil Hardness                                                                Scratch        2H     3H    H     6B    F                                      Cut through    4H     6H    4H    4B    2H                                     Sward Rocker Hardness                                                          % of glass     4%     28%   28%   4%    30%                                    MIBK resistance                                                                               NA     NA    NA    NA    NA                                     24 hour chemical resistance                                                    H.sub.2 O      NA     NA    Soft  Soft  S.Soft                                 20% NaOH       S.Soft NA    NA    NA    NA                                     40% H.sub.2 SO.sub.4                                                                          NA     NA    NA    Swollen                                                                              NA                                     __________________________________________________________________________

Table I shows a comparison of several properties of the various compositions prepared in accordance with the present invention. The solution appearance is a visual determination of the interpenetrating urethane-linking radiation sensitive resin composition prior to the curing operation. The film appearance shows the nature of the film on the substrate surface following the radiation and thermal curing operation. As the compositions of the present invention have several uses it is not necessary that solution appearance be clear or that film appearance be smooth but rather the properties of the cured compositions of the present invention may be determined from Table I to provide the desired effect.

The adhesion test determined on black plate and Bonderite gives a relative comparison of the amount of the film which may be removed from the respective substrates by a cross hatched network of tape applied over the coating and subsequently removed. A score of 100 indicates that all of the coating may be removed by the tape test while the score of 0 means that none of the coating is removed from the substrate. While most of the black plate tests indicate a 100 percent tape test score this is not necessarily bad as the black plate is the most difficult to adhere a coating on. In contrast Examples XI through XV and XX have very strong adhesion properties on black plate and may thus be used for any surface which has difficult adhesion properties. In contrast the Bonderite 100 surface ordinarily gives relatively strong adhesion to coatings and thus most of the composition of the present invention give 0 percent tape loss on this material.

The GE extensibility test is an ASTM method of determining the flexibility of the coating on the substrate. The Gardner reverse impact test on Bonderite 100 indicates the force in inch pounds required to damage a film applied to the substrate.

The pencil hardness test indicates the scratch resistance of the resin coating with 9H being the hardest and 6B being the softest. The Sward Rocker Hardness test indicates the relative hardness of the resin coating on the substrate versus that of glass.

The MIBK resistance test indicates the effect on the coating by methyl isobutyl ketone which has been rubbed on the coated substrate. Generally lightly crosslinked or incompletely cured coatings will soften under the MIBK test. The abreviation NA in the tables indicates no affect. V, S, and SS indicate very, slightly, and slightly soft respectively.

The 24 hour chemical resistance test indicates the effect of water, a 20% sodium hydroxide, and a 40% sulfuric acid on the coating surface.

EXAMPLES XXVII-XXXII

Examples XXVII through XXX inclusive are identical to Example XXIV with the exception that the 1,6-hexane diol diacrylate has been replaced on equal weight basis by the reactive diluents listed below.

    ______________________________________                                         Example No.                                                                              Reactive Diluent Source                                              ______________________________________                                         XXVII     2-ethylhexyl acrylate                                                                           Rohm & Haas                                         XXVIII    Isodecylacrylate Haven                                               XXIX      N-vinyl-2-pyrrolidone                                                                           GAF                                                 XXX       Diethylene glycol di-                                                          acrylate         Sartomer                                            XXXI      Trimethylol propane tri-                                                       acrylate         Celanese                                            XXXII     Diallyl maleate  Borden Chem.                                        ______________________________________                                    

The properties of the compositions prepared according to the present invention for Examples XXVII through XXXII are reported in Table II below. It can be seen that the compositions defined in the examples given in Table II provide excellent coating qualities.

                                      TABLE II                                     __________________________________________________________________________     VARIOUS REACTIVE DILUENTS                                                                                        XXX   XXXI                                                  XXVII  XXVIII                                                                              XXIX   Diethylene                                                                           Trimethylol                                                                           XXXII                                          2-Ethylhexyl                                                                          Isodecyl                                                                            N-vinyl-                                                                              Glycol                                                                               Propane                                                                               Diallyl                         Reactive Diluent Name                                                                         acrylate                                                                              acrylate                                                                            2-pyrrolidone                                                                         Diacrylate                                                                           Triacrylate                                                                           Maleate                         __________________________________________________________________________     Pluracol PEP450 (OH eq. wt.)                                                                  100.7  100.7                                                                               100.7  100.7 100.7  100.7                           Weight in (gms)                                                                               10.7   10.7 10.7   10.7  10.7   10.7                            Reactive Diluent (gms)                                                                        12.5   12.5 12.5   12.5  12.5   12.5                            Desmodur N100                                                                  Weight in (gms)                                                                               19.1   19.1 19.1   19.1  19.1   19.1                            Vicure 10 at 5 phr                                                                            0.63   0.63 0.63   0.63  0.63   0.63                            Hexabutyl ditin at 0.3%                                                                       0.09   0.09 0.09   0.09  0.09   0.09                            Solution Appearance                                                                           Clear  Hazy Clear  Clear Clear  Clear                           Film Appearance                                                                               V.Hazy V.Hazy                                                                              V.S.Craters                                                                           Smooth                                                                               Smooth Smooth                          Adhesion % Loss Tape Test:                                                     Black Plate    100    100   0     70    100    0                               Bonderite 100   0      0    0      0     0     0                               G.E. Extensibility                                                             Black Plate    20-40  20-40                                                                               60     40-60 10-20  40-60                           Gardner Reverse Impact                                                         Bonderite 100  160    160  160    160   75-80  160                             Pencil Hardness                                                                Scratch        H      F    3H     2H    3H     F                               Cut through    2H     H    6H     5H    6H     F                               Sward Rocker Hardness                                                          % of glass     26     14   30     30    40     2                               MIBK resistance                                                                               NA     NA   NA     NA    NA     S.Soft                          24 hour chemical resistance                                                    H.sub.2 O      S.Soft S.Soft                                                                              Soft   S.Soft                                                                               V.S.Soft                                                                              Soft                            20% NaOH       NA     NA   NA     NA    NA     V.Soft                          40% H.sub.2 SO.sub.4                                                                          S.Soft V.S.Soft                                                                            V.Soft NA to NA     Soft                                                              V.V.S.Soft                                   __________________________________________________________________________

EXAMPLES XXXIII-XXXVII

The following Examples are identical to the composition of Example XXIV with the exception that the polyisocyanate in Example XXIV has been replaced on an equivalent basis with the materials listed below.

    ______________________________________                                                                   Source and                                           Example No.  Polyisocyanate                                                                              Description                                          ______________________________________                                         XXXIII       trimethyl hexa-                                                                methylene    VEBA - aliphatic C-9                                              diisocyanate diisocyanate                                         XXXIV        C17 (NCO)2   GMCI - aliphatic C17                                                           diisocyanate                                         XXXV         DDI 1410     GMCI - aliphatic C36                                                           diisocyanate                                         XXXVI        IPDI         VEBA - isophorone                                                              diisocyanate                                         XXXVII       TDI          Allied - toluene                                                               diisocyanate                                         ______________________________________                                    

The properties of the compositions prepared above are reported in Table III.

                                      TABLE III                                    __________________________________________________________________________     VARIOUS POLYISOCYANATES                                                                      XXXIII XXXIV  XXXV  XXXVI XXXVII                                 Isocyanate Name                                                                              TMDI   C.sub.17 (NCO).sup.2                                                                  DDI® 1410                                                                        IPDI  TDI                                    __________________________________________________________________________     Equivalent weight                                                                            105.1  161.0  302.1 111.2 87.1                                   Equivalents   .1     .1     .1    .1    .1                                     Weight (gms)  10.51  16.1   30.21 11.12 8.71                                   Pluracol PEP450                                                                              10.07  10.07  10.07 10.07 10.07                                  1,6-hexanediol diacrylate                                                                    8.82   11.22  17.26 9.08  8.05                                   Vicure 10     0.44   0.56   0.86  0.45  0.40                                   Hexabutyl ditin                                                                              0.06   0.08   0.12  0.06  --                                     Solution Appearance                                                                          Clear  S.Haze V.Hazy                                                                               Clear Clear                                                (low visc)                                                                            (low visc)                                                                            (low visc)                                                                           (low visc)                                                                           (low visc)                             Film Appearance                                                                              Some Craters                                                                          Grainy S.Hazy                                                                               Smooth                                                                               Smooth                                 Adhesion % Loss Tape Test:                                                     Black Plate   65     15     75    50    100                                    Bonderite 100  0      3     10     0     0                                     G.E. Extensibility                                                             Black Plate   40-60  60     40-60 40-60  60                                    Gardner Reverse Impact                                                         Bonderite 100 160    160    160   160   160                                    Pencil Hardness                                                                Scratch       F      H      F     4H    4H                                     Cut through   5H     H      F     6H    7H                                     Sward Rocker Hardness                                                          % of glass    36     8      2     46    56                                     MIBK Resistance                                                                              NA     NA     V.S.Soft                                                                             NA    NA                                     24 hour chemical resistance                                                    H.sub.2 O     NA     NA     NA    NA    NA                                     20% NaOH      S.Soft S.Soft Soft  NA    NA                                     40% H.sub.2 SO.sub.4                                                                         NA     NA     NA    NA    NA                                     __________________________________________________________________________

The compositions reported in Table III show that desirable coatings are obtained through the use of various polyisocyanates when the compositions are formed in accordance with the methods of the present invention.

EXAMPLES XXXVIII-XLIII

The above examples are identical to Example XXIV with the exception that the present examples have been varied in the content of the reactive diluent (radiation curable) to the urethane linked components (thermal curable).

    ______________________________________                                                          Percent Radiation                                                              Curable to Urethane Linked                                    Example No.      (Thermal Cure)                                                ______________________________________                                         XXXVIII          100          0                                                XXXIX            80          20                                                XL               60          40                                                XLI              40          60                                                XLII             20          80                                                XLIII             0          100                                               ______________________________________                                    

The results obtained in forming the above compositions are reported in Table 4 below.

                                      TABLE IV                                     __________________________________________________________________________     RATIO VARIATIONS (RADIATION CURABLE TO THERMAL CURABLES)                       Example Number                                                                               XXXVIII                                                                              XXXIX                                                                               XL   XLI  XLII XLIII                                  __________________________________________________________________________     Percent - Radiation Cure                                                                     100   80   60   40   20    0                                     to Thermal Curable                                                                            0    20   40   60   80   100                                    Desmodur N-100                                                                 Equivalent    --    .1   .1   .1   .1   .1                                     Weight (gms)  --    19.1 19.1 19.1 19.1 19.1                                   Pluracol PEP 450 (Eq. Wt.)                                                                   --    100.7                                                                               100.7                                                                               100.7                                                                               100.7                                                                               100.7                                  Weight (gms)  --    10.07                                                                               10.07                                                                               10.07                                                                               10.07                                                                               10.07                                  1,6-hexanediol diacrylate                                                                    20.0  116.7                                                                               43.76                                                                               19.45                                                                               7.29 --                                     Vicure 10     1.0   5.83 2.19 0.97 0.36 --                                     Hexabutyl ditin                                                                              --    0.099                                                                               0.088                                                                               0.088                                                                               0.088                                                                               0.088                                  Solution Appearance                                                                          Clear Clear                                                                               Clear                                                                               Clear                                                                               S.Haze                                                                              Hazy                                                 (low visc)                                                       Film Appearance                                                                              Smooth                                                                               Smooth                                                                              Smooth                                                                              Smooth                                                                              Smooth                                                                              Wrinkled                               Adhesion % Loss Tape Test:                                                     Black Plate   100   100  100  100  85   10                                     Bonderite 100  5     0    0    0    0    0                                     G.E. Extensibility                                                             Black Plate   2-5   2-5  20-40                                                                               20-40                                                                               60   60                                     Gardner Reverse Impact                                                         Bonderite 100 4     4    120-130                                                                             80-100                                                                              130-140                                                                             160                                    Pencil Hardness                                                                Scratch       3H    3H   2H   4H   H    F                                      Cut through   4H    5H   5H   6H   5H   5H                                     Sward Rocker Hardness                                                          % of glass    12    42   52   40   36   32                                     MIBK resistance                                                                              NA    NA   NA   NA   NA   NA                                     24 Hour Chemical Resistance                                                    H.sub.2 O     V.S.Soft                                                                             NA   NA   NA   NA   NA                                     20% NaOH      S.Soft                                                                               V.S.Soft                                                                            NA   NA   V.S.Soft                                                                            S.Soft                                 40% H.sub.2 SO.sub.4                                                                         NA    NA   NA   NA   NA   NA                                     __________________________________________________________________________

The above results reported in Table IV indicate that particularily desirable interpenetrated urethane linked coating compositions are obtained when the weight ratio of the radiation curable to the thermal curable components is from about 80:20 to about 20:80.

As previously stated the compositions of the present invention form tough, hard coatings from a low viscosity interpenetrating radiation sensitive resin composition which cures substantially free from solvent emission. 

What is claimed is:
 1. An interpenetrating radiation-sensitive resin composition comprising:(a) from about 40% to about 90% by weight of a saturated polyol which is a hydroxy functional acrylic copolymer of:(1) methyl methacrylate; (2) butyl acrylate, and (3) hydroxyethyl acrylate and, (b) from about 10% to about 60% by weight of a reactive diluent having a radiation sensitive pi bond and having a boiling point greater than that of benzene, and mixtures thereof said reactive diluent being a fully substituted polyacrylate or polymethacrylate of a polyfunctional alcohol.
 2. The composition of claim 1 wherein the reactive diluent is selected from the group consisting of diol diacrylates, triol triacrylates, and tetrol tetraacrylates and mixtures thereof.
 3. The composition of claim 2 wherein the reactive diluent is selected from the group consisting of:(a) 1,6-hexane diol diacrylate; (b) ethylene glycol diacrylate; (c) trimethylol propane triacrylate; (d) triethylene glycol diacrylate; (e) neopentyl diol diacrylate; and (f) pentaerythritol tetraacrylate,and mixtures thereof.
 4. The composition of claim 3 wherein the reactive diluent is 1,6-hexane diol diacrylate at from about 20% to about 50% by weight and from about 50% to about 80% by weight of a hydroxyfunctional copolymer of:(a) methyl methacrylate, (b) butyl acrylate, and (c) hydroxyethyl acrylate in a molar ratio of a:b:c of from about 4:1:1 to about 1:4:3.
 5. An interpenetrating urethane-linking, radiation-sensitive resin composition comprising:(a) from about 40% to about 90% by weight of a saturated polyol which is a hydroxy functional acrylic copolymer of:(1) methyl methacrylate; (2) butyl acrylate, and (3) hydroxyethyl acrylate and, (b) from about 10% to about 60% by weight of a reactive diluent selected from the group consisting of the fully substituted polyacrylates and polymethacrylates of poly-functional alcohols, 2-ethylhexylacrylate, isodecylacrylate, diallyl maleate, styrene, divinylbenzene, vinyl acetate, and N-vinyl-2-pyrrolidone, and mixtures thereof; and, (c) from about 80% to about 120% on a hydroxylisocyanate equivalent basis of a polyisocyanate.
 6. The composition of claim 5 wherein the sum of the polyisocyanate functionality and hydroxy functionality is greater than four.
 7. The composition of claim 5 wherein the reactive diluent is 1,6-hexane diol diacrylate.
 8. The composition of claim 7 wherein the reactive diluent is a mixture of 1,6-hexane diol diacrylate and N-vinyl 2-pyrrolidone in a respective weight ratio of from about 4:1 to about 1:4.
 9. The composition of claim 8 wherein the polyisocyanate is present at from about 95% to 105% on a hydroxyl-isocyanate equivalent basis.
 10. The composition of claim 9 wherein the polyisocyanate is selected from the group consisting of diisocyanates and triisocyanates and mixtures thereof.
 11. The composition of claim 10 wherein the polyisocyanate is selected from the group consisting of:(a) toluene diisocyanate; (b) xylene diisocyanate; (c) isophorone diisocyanate; (d) hexamethylene diisocyanate; (e) the triisocyanate adduct of hexamethylene diisocyanate and water, (f) trimethyl hexamethylene diisocyanate, (g) aliphatic diisocyanates having from 12 to 40 carbon atoms in the aliphatic moiety;and mixtures thereof.
 12. The composition of claim 5 wherein the weight ratio of (a) plus (c) to (b) is from about 80:20 to about 20:80. 